Soldabilidad de un acero microaleado utilizando el proceso Smaw y metal de aporte ferrítico de alta resistencia

In this research was studied the weldability of Q&T armor steel MIL A46100 (Fe; 0.28%C; 0.30%Cr; 0.24%Mo y 0.2%Ni), with AWS E11018M filler metal and SMAW manual process, through relations generated between of microstructure, process variables, mechanical properties (tension, toughness impact Charpy V and microhardness); in addition was evaluated the susceptibility of the HIC through CTS (Controlled Thermal Severity) test and H plates on the weldments and the performance of service (ballistic performance), in different input heats, named: high and low. Has been established the incidence of the input heat on the properties and the service performance.En esta investigación se estudió la soldabilidad de uniones de un acero templado y revenido para blindajes del tipo MIL A46100 (Fe; 0,28% C; 0,30% Cr; 0,24% Mo y 0,20% Ni), usando metal de aporte AWS E11018M, y el proceso Smaw (soldadura al arco eléctrico con electrodo revestido), a través de relaciones generadas entre microestructura, variables del proceso y propiedades mecánicas (tracción, impacto Charpy V y microdurezas), en juntas de soldadura. Asimismo se evaluó el agrietamiento en frío a través de dos ensayos (severidad térmica controlada y placa H), y el desempeño en servicio (balístico) de las mismas, obtenidas al practicar uniones con dos entradas de calor, denominadas alta y baja. Se estableció la incidencia del aporte calórico sobre las propiedades y el desempeño