ЗАВИСИМОСТЬ ДЕФОРМАЦИОННОГО СОСТОЯНИЯ ПЛЕНОК GaAs НА ВИЦИНАЛЬНЫХ ПОДЛОЖКАХ Si(001) ОТ СПОСОБА ФОРМИРОВАНИЯ ПЕРВЫХ МОНОСЛОЕВ ПРОСЛОЙКИ GaP

A significant dependence of the strain state of GaAs film lattice grown by molecular−beam epitaxy (MBE) on the nucleation method of early GaP buffer layers (50 nm) on the vicinal substrate Si(001) 4° around the <011> axis was discovered. GaP growth started layer−by−layer with a gallium or a phosphorus sublayer. If GaP nucleated with a gallium sublayer, the GaAs film has a significant lattice rotation around the <011> axis. If the buffer starts forming with a phosphorus layer the GaAs film evidently rotates around the <001> axis. The film relaxation degree ex- ceeds 100%, and the film is in a laterally strained state. Analysis was carried out using the triclinic distortion model. A reciprocal space scattering map was obtained using X−ray diffraction in a three−axis low resolution setup. The map clearly shows that the GaAs film lattice is rotated.Выявлена существенная зависимость деформационного состояния кристаллической решетки пленок GaAs, выращенных методом молекулярнолучевой эпитаксии от способа зарождения первых слоев прослойки GaP (50 нм) на вицинальной подложке Si(001) 4° вокруг оси <011>. Рост GaP начинался послойно с галлиевого или фосфорного подслоя. Установлено, что в случае зарождения GaP с галлия, пленка GaAs имеет значительный поворот кристаллической решетки вокруг направления <011>. При фор- мировании прослойки с фосфорного подслоя заметен поворот пленки GaAs вокруг <001>. Степень релаксации пленки составляет более 100 %, она находится в латерально растянутом состоянии. Анализ проведен с использованием модели триклинных искажений. Представлена карта рассеяния в обратном пространстве, полученная с помощью рентгеновской дифрактометрии в трехосевой схеме малого разрешения. На карте явно виден факт поворота кристаллической решетки пленки GaAs.