Add to ORKGSolid film lubricants of radio frequency sputtered molybdenum disulfide (MoS2) were applied to silve...
Molybdenum disulfide films 300 to 400 A thick were rf sputtered on aluminum and nickel surfaces at e...
The glow discharge or ion assisted vacuum deposition techniques, primarily sputtering and ion platin...
Thin sputter deposited MoS2 films in the 2000 to 6000 A thickness range have shown excellent lubrica...
The present practices, limitations, and understanding of thin sputtered MoS2 films are reviewed. Spu...
It is shown that the tribological quality of MoS2 lubricant films formed by magnetron sputtering is ...
Potential and present sputtering technology is discussed as it applies to the deposition of solid fi...
Sputtered molybdenum disulfide film deposition and friction characteristics in vacuu
Molybdenum disulfide (MoS2) is a good solid film lubricant for vacuum and spacecraft applications. T...
Three microstructural growth stages of sputtered MoS2 films were identified with respect to film thi...
Sputtered MoS2 films from 300 A to 20,000 A thick were deposited on metal and glass surfaces. The su...
AuMoS2 films 0.02 to 1.2 microns thick were sputtered from target compacted from 5 wt % Au + 95 wt %...
An optical microscope was used to study the lubrication and failure mechanisms of rubbed (burnished)...
MoS2 thin films are sputter-deposited in different conditions in order to obtain well-defined micros...
An optical microscope was used to study the lubrication and failure mechanisms of rubbed MoS2 films ...
Solid film lubricants of radio frequency sputtered molybdenum disulfide (MoS2) were applied to silve...
Molybdenum disulfide films 300 to 400 A thick were rf sputtered on aluminum and nickel surfaces at e...
The glow discharge or ion assisted vacuum deposition techniques, primarily sputtering and ion platin...
Thin sputter deposited MoS2 films in the 2000 to 6000 A thickness range have shown excellent lubrica...
The present practices, limitations, and understanding of thin sputtered MoS2 films are reviewed. Spu...
It is shown that the tribological quality of MoS2 lubricant films formed by magnetron sputtering is ...
Potential and present sputtering technology is discussed as it applies to the deposition of solid fi...
Sputtered molybdenum disulfide film deposition and friction characteristics in vacuu
Molybdenum disulfide (MoS2) is a good solid film lubricant for vacuum and spacecraft applications. T...
Three microstructural growth stages of sputtered MoS2 films were identified with respect to film thi...
Sputtered MoS2 films from 300 A to 20,000 A thick were deposited on metal and glass surfaces. The su...
AuMoS2 films 0.02 to 1.2 microns thick were sputtered from target compacted from 5 wt % Au + 95 wt %...
An optical microscope was used to study the lubrication and failure mechanisms of rubbed (burnished)...
MoS2 thin films are sputter-deposited in different conditions in order to obtain well-defined micros...
An optical microscope was used to study the lubrication and failure mechanisms of rubbed MoS2 films ...
Solid film lubricants of radio frequency sputtered molybdenum disulfide (MoS2) were applied to silve...
Molybdenum disulfide films 300 to 400 A thick were rf sputtered on aluminum and nickel surfaces at e...
The glow discharge or ion assisted vacuum deposition techniques, primarily sputtering and ion platin...