The Combined Effects of Curing and Environmental Exposure on Fracture Properties of Woven Carbon/Epoxy Laminates

This paper concerns a study of the combined effects of curing conditions and environmental exposure on the ultimate properties of two commercial woven carbon/epoxy laminates. Curing parameters (heating rate and applied pressure) were varied so as to obtain six different conditions for each material. Moisture saturation was also achieved by exposing some of the cured samples to environmental conditions of 70°C and 95% relative humidity. Four different tests (tensile, impact, Mode I and Mode II interlaminar fracture resistance) were therefore performed, and the results obtained on the different materials before and after moisture saturation compared. Neither curing pressure nor heating rate nor moisture absorption were observed to have any practical effect on tensile and impact properties. On the contrary, one noticeable effect was the interlaminar fracture resistance of the laminates. The results are discussed and interpreted in terms of damage formation and stress intensification mechanisms