In-Depth Analysis of the Nonuniform Chain Microstructure of Multiblock Copolymers from Chain-Shuttling Polymerization

The nonuniform molecular architecture of ethylene/1-octene multiblock copolymers (O-MBCs) synthesized by the chain shuttling technology is investigated. The samples consist of chains characterized by alternating hard (crystalline) and soft (amorphous) blocks, corresponding to random ethylene/1-alkene copolymers with a low and high comonomer content, respectively. The chains are nonuniform as the distribution in the length and number of blocks per chain are statistical and vary from chain to chain. A clear-cut investigation of the inter-and intrachain constitutional heterogeneity of O-MBCs is performed by carrying out, at first, a sequential and exhaustive solvent fractionation procedure in boiling solvents, that is, diethyl ether, n-hexane, and cyclohexane. Successively, the unfractionated samples and the corresponding fractions are subjected to analytical crystallization elution fractionation (aCEF), solution 13C NMR, differential scanning calorimetry, and wide-and small-angle X-ray scattering (SAXS) analyses. Four fractions of increasing average ethylene content, hard block content, and degree of crystallinity are obtained, that is, a fraction soluble in diethyl ether (sEE), a fraction insoluble in diethyl ether/soluble in n-hexane (iEE-sC6), a fraction insoluble in n-hexane/soluble in cyclohexane (iC6-sCC6), and a fraction insoluble in cyclohexane (iCC6). The results of aCEF and 13C NMR analysis highlight that the multiblock chain microstructure of the O-MBCs corresponds to a statistical distribution of the length of hard and soft blocks that occurs not only at an interchain level but also at an intrachain level. SAXS measurements essentially confirm the results of the microstructural analysis and allow achieving a quantitative description of the constitutional heterogeneity affecting O-MBCs at the intramolecular level. In particular, it is shown that for the inferior fractions (sEE and iEE-sC6), the chains include hard blocks of low molecular mass (