The effect of water on the viscosity of a haplogranitic melt under P-T-X- conditions relevant to silicic volcanism

The viscosities of hydrous haplogranitic melts synthesized by hydrothermal fusion at 2 kbar pressure and 800 to 1040°C have been measured at temperatures just above the glass transition and at a pressure of 1 bar using micropenetration techniques. The micropenetration viscometry has been performed in the viscosity range of 109 Pa s to 1012 Pa s. The samples ranged in water content from 0.4 to 3.5 wt%. For samples with up to 2.5 wt% H2O, the water contents have been determined using infrared spectroscopy obtained before and after each viscometry experiment to be constant over the duration of the measurements. Above this water content a measurable loss of water occurs during the viscometry. The viscosity data illustrate an extremely nonlinear decrease in viscosity with added water. The viscosity drops drastically with the addition of 0.5 wt% of water and then shallows out at water contents of 2 wt%. An additional viscosity datum point obtained from the analysis of ßuid inclusions in a water-saturated HPG8 confirms a near invariance of the viscosity with the addition of water between 2 and 6 wt%. These measurements may be compared directly with the data of Hess et al. (1995, in press) for the effects of excess alkali and alkaline earth oxides on the viscosity of HPG8 (also obtained at 1 bar). The viscosity of the melts, compared on an equivalent molar basis, increases in the order H2O<(Li 2O<Na2O<K2O<Rb2O,Cs2O<BaO<SrO<CaO<MgO