Spawanie stali niskostopowej z mikrojetowym chłodzeniem

Low alloy steel is used for many important structures. In that material there is a small amount of carbon and controlled percentage of alloy elements such as Ni, Mn, Mo, Si in steel and welded joints. Especially Ni, Mo, O could be treated as elements positively influencing impact toughness of welded structures. Metallographic structure of weld metal deposit (WMD) having composition of 400 ppm O and 2% Ni or 0.4% Mo and is very beneficial because of high percentage of acicular ferrite (until 65%) and thus WMD has good mechanical properties. For a long time researchers were putting two questions: how to lift percentage of AF in weld, and further what consequence that fact gives? Micro jet technology could be treated as a chance to resolve that problem. The present paper describes the influence of artificially lifted amount of acicular ferrite in WMD (above 65%) on the behaviour of steel weld properties using micro-jet cooling.Do ważnych konstrukcji używana jest stal niskostopowa, bardzo często z małą ilością węgla i kontrolowaną zawartością pierwiastków stopowych, takich jak Ni, Mn, Mo, Si. Zwłaszcza Ni, Mo, O są uważane za pierwiastki pozytywnie wpływające na udarność spawanych konstrukcji. Struktura metalograficzna stopiwa posiadającego 400 ppm O i 2% Ni albo 0,4% Mo korzystnie wpływa na własności mechaniczne złącza z powodu wysokiej zawartości drobnoziarnistego wewnatrz-ziarnowego ferrytu (ferryt AF) w stopiwie (do 65%) i przez to na dobre własności mechaniczne. Przez długi czas badacze zadają dwa pytania: jak można podnieść zawartość ferrytu AF w spoinie i jakie to przyniesie następstwa? Technologie microjetowa uważa się za szansę na rozwiązanie tego problemu. Przedstawiony artykuł opisuje wpływ sztucznie zawyżonej zawartości ferrytu AF w stopiwie (ponad 65%) na właściwości stalowego złącza ze względu na zastosowanie mikrojetowego chłodzenia