Elevated Temperature, Notched Compression Performance of Out of Autoclave Processed Composites

Curved honeycomb sandwich panels composed of carbon fiber reinforced toughened-epoxy polymer facesheets are being evaluated for potential use as payload fairing components on the NASA heavy-lift space launch system (HL-SLS). These proposed composite sandwich panels provide the most efficient aerospace launch structures, and offer mass and thermal advantages when compared with existing metallic payload fairing structures. NASA and industry are investigating recently developed carbon fiber epoxy prepreg systems which can be fabricated using out-of autoclave (OOA) processes. Specifically, OOA processes using vacuum pressure in an oven and thereby significantly reducing the cost associated with manufacturing large (up to 10 m diameter) composite structures when compared with autoclave. One of these OOA composite material systems, CYCOM(R) 5320-1, was selected for manufacture of a 1/16th scale barrel portion of the payload fairing; such that, the system could be compared with the well-characterized prepreg system, CYCOM(R) 977-3, typically processed in an autoclave. Notched compression coupons for each material were obtained from the minimum-gauge flat laminate [60/-60/0]S witness panels produced in this manufacturing study. The coupons were also conditioned to an effective moisture equilibrium point and tested according to ASTM D6484M-09 at temperatures ranging from 25 C up to 177 C. The results of this elevated temperature mechanical characterization study demonstrate that, for thin coupons, the OHC strength of the OOA laminate was equivalent to the flight certified autoclave processed composite laminates; the limitations on the elevated temperature range are hot-wet conditions up to 163 C and are only within the margins of testing error. At 25 C, both the wet and dry OOA material coupons demonstrated greater OHC failure strengths than the autoclave processed material laminates. These results indicate a substantial improvement in OOA material development and processing since previous studies have consistently reported OOA material strengths on par or below those of autoclave processed composite laminates