Influência de diferentes espessuras no grau de conversão de uma resina adesiva

Aim: the purpose of this study was to evaluate the degree of conversion (DC) of different thicknesses (1, 2, 3 and 4 mm) of a translucent dental adhesive resin Materials and Methods: the degree of conversion (DC) of adhesive resins was measured by Fourier Transform Infrared Spectroscopy (FTIR) equipped with an attenuated total reflectance device (ATR). It were used four matrices of polyvinylsiloxane with dimensions of 1; 2; 3 or 4 mm in thickness and 7 mm in diameter each one to contain the dispensed adhesive (n = 3) on the diamond crystal of the ATR device. The data were analyzed by one-way ANOVA and Student-Newman-Keels’ post hoc test (α=0.05). Results: specimens of 1 mm of thickness showed statistically higher DC (62.19 ± 0.20) compared to the other groups (p0.05), but groups of 2 and 3 mm showed higher DC than the group of 4 mm (pObjetivos: o objetivo desse trabalho foi avaliar o grau de conversão (GC) de diferentes espessuras (1; 2; 3 e 4 mm) de uma resina adesiva translúcida de uso odontológico. Materiais e métodos: o GC de uma resina adesiva translúcida foi avaliado por meio de espectroscopia no infravermelho por transformada de Fourier (FTIR) acoplado a um dispositivo de refletância total atenuada (ATR). Foram utilizadas quatro matrizes de polivinilsiloxano de 1; 2; 3 ou 4 mm de espessura por 7 mm de diâmetro cada uma para conter o adesivo dispensado (n = 3) sobre o cristal de diamante do dispositivo de ATR. ANOVA de uma via e teste de comparações múltiplas de Student-Newman-Keuls foram utilizados com um nível de significância estatística de 5%. Resultados: espécimes de 1 mm de espessura apresentaram estatisticamente maiores valores de GC (62,19± 0,20) comparado aos demais grupos (p0,05), mas foram maiores que o grupo de 4mm (p>0,05). Conclusão: é necessária a padronização da espessura dos espécimes submetidos ao ensaio de avaliação de GC por FTIR-ATR