High-pressure magnetization of the heavy-Fermion system CeRu2Si 2 .

The low-temperature magnetization of single-crystal CeRu2Si 2 has been investigated under hydrostatic pressures up to 6 kbar. The results reveal an extremely rapid decrease of the magnetic susceptibility χ∥ (T →0) for H applied along the c-axis, at a rate of about —17% per kbar. A strong correlation (χ∥ (0) Tmax ≃ const. ) is found between the pressure-variations of the susceptibility at T = 0 and the temperature of the susceptibility maximum. The data for χ∥ (T) T can be represented by a single curve in terms of the reduced variable T/Ts (P), in accordance with single-impurity Kondo theories. The magnetic anisotropy χ∥/χ ⊥decreases, as expected for a system approaching the mixed-valence regime, but alternative explanations are also considered. The results are compared to other high-pressure studies on the same material and to the effects produced by alloying.L'aimantation de CeRu2Si2 monocristallin à basse température a été mesurée sous pression hydrostatique jusqu'à 6 kbar. Les résultats révèlent une décroissance extrêmement rapide de la susceptibilité magnétique χ∥ (T → 0) pour H suivant l'axe c, à raison d'environ — 17 % par kilobar. On constate une forte corrélation (χ∥ (0 ) Tmax ≃ cst.) entre la variation en pression de la susceptibilité à T = 0 et la température du maximum de susceptibilité. Les données pour χ∥ (T) T peuvent être représentées par une courbe unique rapportée à une variable réduite T/Ts (P) , en accord avec les théories Kondo à une impureté. L'anisotropie magnétique χ∥ χ⊥ décroît comme on s'y attend pour un système s'approchant du régime de valence intermédiaire, mais d'autres explications sont également envisagées. Les résultats sont comparés à d'autres études du même matériau sous haute pression ainsi qu'aux effets observés dans certains de ses alliages