Comportement dissymétrique des dislocations entre traction et compression dans des superalliages base-nickel

The elementary shearing configurations of γ' precipitates in single crystals of Nibased superalloys have been studied after creep and dynamical experiments using TEM techniques. A change of configurations has been observed between tension and compression. This tension/ compression asymetry may be explained by considering the interplay between the crossing of the γ/γ' interface by elementary Shockley dislocations and the effect of the applied stress on the dissociation width of matrix dislocations. An original model of shear of precipitates by dissociated matrix dislocations is proposed and an understanding of the dependence of the shearing processes with the temperature is provided.La microscopie électronique en transmission a été utilisée pour étudier les configurations élémentaires de cisaillement des précipités γ' dans des superalliages base nickel après des essais de fluage et des essais dynamiques. Un changement de configuration a été observé entre les essais de traction et de compression. Cette assymétrie traction/compression peut être expliquée en considérant la résultante de deux effets: le franchissement de l'interface par des partielles de Shockley et l'effet de la contrainte appliquée sur la largeur de dissociation des dislocations de matrice. Un modèle original de cisaillement des précipités par des dislocations de matrice a été proposé ainsi qu'une explication de la dépendence vis à vis de la température des processus de cisaillement