Magnetomechanical coupling coefficient as a function of magnetic bias field in Fe23.5Cu1W3Si15.5B7 alloy in as-quenched state and after annealing in vacuum for 1 h from 400 to 500°C were investigated. The maximum values of the k coefficient were equal to 0.10-0.14 for as-quenched state and increased to 0.61 after annealing at 450°C. The results were somewhat worse than those with Nb instead of the W. Nanocrystallization begins after annealing above 450°C and the magnetostriction rapidly drops and the magnetomechanical coupling practically vanishes after annealing at 520°C
The magnetomechanical coupling coefficient (k) of amorphous Fe(73.5)Cu(1)Nb(3)Si1(5.5)B(7) alloy str...
The magnetomechanical coupling coefficient (k) of amorphous Fe(73.5)Cu(1)Nb(3)Si1(5.5)B(7) alloy str...
The magnetostriction and magnetomechanical coupling (k) in the Fe73.5Cu1Nb3Si13.5B9 strips annealed ...
Magnetomechanical coupling coefficient as a function of magnetic bias field in Fe23.5Cu1W3Si15.5B7 a...
Magnetomechanical coupling coefficient as a function of magnetic bias field in Fe23.5Cu1W3Si15.5B7 a...
Magnetic field dependences of magnetomechanical coupling coefficient and moduli of elasticity in Fe7...
Magnetic field dependences of magnetomechanical coupling coefficient and moduli of elasticity in Fe7...
The Fe73.5Cu1Nb1Ta2Si13.5B9 samples were measured in as-quenched state and after annealing for 1 h i...
The Fe73.5Cu1Nb1Ta2Si13.5B9 samples were measured in as-quenched state and after annealing for 1 h i...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The magnetomechanical coupling coefficient (k) of amorphous Fe(73.5)Cu(1)Nb(3)Si1(5.5)B(7) alloy str...
The magnetomechanical coupling coefficient (k) of amorphous Fe(73.5)Cu(1)Nb(3)Si1(5.5)B(7) alloy str...
The magnetomechanical coupling coefficient (k) of amorphous Fe(73.5)Cu(1)Nb(3)Si1(5.5)B(7) alloy str...
The magnetostriction and magnetomechanical coupling (k) in the Fe73.5Cu1Nb3Si13.5B9 strips annealed ...
Magnetomechanical coupling coefficient as a function of magnetic bias field in Fe23.5Cu1W3Si15.5B7 a...
Magnetomechanical coupling coefficient as a function of magnetic bias field in Fe23.5Cu1W3Si15.5B7 a...
Magnetic field dependences of magnetomechanical coupling coefficient and moduli of elasticity in Fe7...
Magnetic field dependences of magnetomechanical coupling coefficient and moduli of elasticity in Fe7...
The Fe73.5Cu1Nb1Ta2Si13.5B9 samples were measured in as-quenched state and after annealing for 1 h i...
The Fe73.5Cu1Nb1Ta2Si13.5B9 samples were measured in as-quenched state and after annealing for 1 h i...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The influence of a magnetic field upon magnetostriction and magnetomechanical coupling (k) was measu...
The magnetomechanical coupling coefficient (k) of amorphous Fe(73.5)Cu(1)Nb(3)Si1(5.5)B(7) alloy str...
The magnetomechanical coupling coefficient (k) of amorphous Fe(73.5)Cu(1)Nb(3)Si1(5.5)B(7) alloy str...
The magnetomechanical coupling coefficient (k) of amorphous Fe(73.5)Cu(1)Nb(3)Si1(5.5)B(7) alloy str...
The magnetostriction and magnetomechanical coupling (k) in the Fe73.5Cu1Nb3Si13.5B9 strips annealed ...