Оцінка впливу фізико-хімічних факторів на корозійну активність води

The paper investigated corrosion processes and determined the level of various aqueous media activity towards metals. Corrosion rate was determined by a manometric method and polarization resistance method. Tap water, artesian water and standard test solution were used as media of comparisons. The influence of pH, temperature and salinity on the rate of metals corrosion was defined. It was found that corrosion activity of neutral aqueous medium depends on the concentration of dissolved oxygen and the content of salt anions in water. It was proved that dissolved inorganic salts significantly accelerate corrosion process. It was found that at the temperature of 20 ºC, with decreased oxygen concentration in static conditions, corrosion rate decreases. It was shown that at high temperatures, the initial concentration of oxygen as well as pH medium, have little effect on corrosion activity of water, since in this case, corrosion of steel is mainly determined by chemical interaction of metal with water.В работе были исследованы корозионные процессы и определен уровень корозионной активности различных водных сред по отношению к металлам. Определено влияние рН, температуры и минерализации на скорость коррозии металлов. Установлено, что коррозионная активность нейтральной водной среды зависит от концентрации растворенного кислорода и от содержания анионов солей в воде. Доказано, что растворенные неорганические соли существенно ускоряют процес коррозии.В роботі було досліджено корозійні процеси та визначено рівень активності різних водних середовищ щодо металів. Визначено вплив рН, температури та мінералізації на швидкість корозії металів. Встановлено, що корозійна активність нейтрального водного середовища залежить від концентрації розчиненого кисню та від вмісту аніонів солей у воді. Доведено, що розчинені неорганічні солі суттєво прискорюють процес корозії