360 degrees domain walls in magnetic thin films with uniaxial and random anisotropy

X ray photoemission electron microscopy XPEEM and magneto optic Kerr effect MOKE microscopy have been performed on a metal insulator multilayer of [Co80Fe20 t 1.8nm Al2O3 3nm ]9 to image 360 amp; 8728; domain walls DWs along easy and hard axes, respectively. Their creation and annihilation can be directly visualized under application of a magnetic field. XPEEM experiments and micromagnetic simulations show that 360 amp; 8728; DWs occur through the merger of 180 amp; 8728; DWs of opposite chiralities along the easy axis. They are stable even under application of large magnetic fields. Formation of 360 amp; 8728; DWs observed along the hard axis is attributed to symmetry breaking of the coherent spin rotation. Their formation in metal insulator multilayers is explained as being due to the presence of an orientational dispersion of anisotropy axes in the film grains that is comparable to an overall uniaxial anisotropy term. Our results are confirmed numerically using micromagnetic simulation