Study of perovskite solar cells degradation

This thesis studies the degradation of perovskite photovoltaic cells placed in atmospheres of different moisture. Samples with inverse structure: ITO/ PEDOT:PSS/ CH3NH3PbI3–XClX / PC70BM/ Ca/ Al were prepared. Electrical characteristics were measured for 2 months and similar degradation trend was observed for all the samples. Perovskite cell efficiency PCE decreased to 20 % of the initial value in t80= 46±3 days in laboratory, t80=23±1$ days in nitrogen atmosphere and t80=25,7±0,6 dní days in dry atmosphere. For the initial 27 days of the experiment, a faster degradation linked with the decrease of ISC, FF and VOC was observed. After this period, the value of FF has stabilised at 0,777±0,009 % and the value of VOC at 0,70±0,02 % of their original value (in the laboratory atmosphere). Additional fall of PCE resulted only from the decrease of ISC and was slower than in the initial period. From the results acquired, it has emerged that during the experiment, the cell encapsulation provided a sufficient barrier against outer moisture. Residual moisture present in the sctructure, was labeled as the source of the degradation. The moisture is believed to enter with the hygroscopic material PEDOT:PSS during the samples preparation procedure. During the degradation, absorption measurements of photovoltaic cells were executed. The absorption spectra didn't change. That indicates, that the decrease of ISC is not caused by the reduction of light absorption. The thesis also studied the degradation of perovskite solar cells under illumination. The samples were exposed to UV radiation for 55,5 hours. The PCE time of decrease to 20 % of the initial value was t80 = 6±2 days. It was revealed, that UV radiation significantly accelerates the decrease of ISC