Investigation of bond strength and energy absorption capabilities in recyclable sandwich panels

The paper investigates the energy absorption characteristics of honey comb sandwich panels manufactured from recyclable materials. In this study, honeycomb cores were manufactured from sawdust-polypropylene composites. The composites were thermoformed between matched-dies into half hexagonal profiles which were ultrasonically bonded at their nodes and facesheets to form recyclable sandwich panels. As the bonding efficiency at the nodes and the core-to-facing interface will be governed by several process parameters, an L8 partial factorial and full factorial design of experiments (DoE) based on the Taguchi method was used. Single lap shear test was used to determine the shear strength of the bond at the nodes, and climbing drum peel test was used to determine the skin-to-core bonding strength in the sandwich panels. The energy absorption characteristic of the honeycombs was determined experimentally by subjecting them to quasi-static compressive loads. The effect of the thickness-to-length ratio (t/l) of the cell walls on the energy absorption was evaluated using finite element (FE) modelling, and energy absorption maps were constructed for various t/l ratios. Taguchi analysis suggested setting all the parameters at their highest levels to obtain maximum lap shear strength at the nodes and indicated that the hold time has negligible influence, following which a L8 full factorial DoE based on orthogonal arrays was used to maximise the peel load, neglecting the hold time parameter. The results indicated a minor interaction between the welding amplitude and welding time, indicating the increase in welding amplitude should be complimented with the welding time. However, this interaction was marginal compared to the main factor effects