Study of friction and wear of thermoplastic vulcanizates: The correlation with abraded surfaces topology

The work was focused on the study of friction and wear properties of thermoplastic vulcanizates (TPV) based on polypropylene (PP), natural rubber (NR) and styrene butadiene rubber (SBR) compounds containing all common additives and curatives using ball-on-flat method. Pure materials and binary TPV blends of PP/NR, as well those of PP/SBR with the compositions 95/5, 75/25 and 50/50 (in weight %) were compounded and analysed. It is very well known that the coefficient of friction (COF), as well as wear values of pure thermoplastic matrix are significantly lower than those for pure rubber. Thus, it was found that the friction coefficient and wear of TPVs significantly increased in accordance with increased content of rubber material. Surprisingly, NR compared with SBR of similar concentrations in PP matrix, considerably affected wear of samples and the friction coefficient remained almost unaffected. Finally the topology of abraded surfaces were examined by using scanning electron microscopy (SEM) in order to understand the relationship between the COF, wear process and the composition of TPVs. © Published under licence by IOP Publishing Ltd.Operational Program Research and Development for Innovations - European Regional Development Fund (ERDF); national budget of the Czech Republic [CZ.1.05/2.1.00/19.0409]; Ministry of Education, Youth and Sports of the Czech Republic - Program NPU I [LO1504