We have studied the structural and magnetic properties for La1-xCaxMnO3 with x = 0.27 and 0.47 using neutron powder diffraction and magnetization measurements. At room and low temperature, all samples have the orthorhombic structure with space group Pnma. The sample x = 0.47 shows the antiferromagnetic mix a ferromagnetic with the magnetic moment and the Curie temperature are 1.30 µβ and 260 K, respectively while the sample x = 0.27 is a ferromagnetic with the magnetic momentand the Curie temperature are 3.10 µβ and 197 K, respectively
The magnetic properties of La1-σMnO3 depend on the relative concentration of Mn+4/Mn+3 introduced by...
THE EFFECT OFCu-DOPINGON CRYSTAL STRUCTURE AND MAGNETORESISTANCE IN La0.73 Ca0.27 Mn1-y CuyO3 WITH 0...
THE EFFECT OFCu-DOPINGON CRYSTAL STRUCTURE AND MAGNETORESISTANCE IN La0.73 Ca0.27 Mn1-y CuyO3 WITH 0...
THE STRUCTURAL AND MAGNETIC PROPERTIES OF La1-xCaxMnO3WITH x = 0.27 AND 0.47. We have studied the st...
THE STRUCTURAL AND MAGNETIC PROPERTIES OF La1-xCaxMnO3WITH x = 0.27 AND 0.47. We have studied the st...
The La1-xCaxMnO3 series of compounds with antiferromagnetic ground states (x≥1/2) have been extensiv...
We studied the crystal and magnetic structure of the La1 xCaxMnO3 compound for 0.11 lt;or x lt;or 0...
The crystal and magnetic structures of La0.70Ca0.30CryMn1 12yO3 for y=0.70, 0.50, and 0.15 have been...
We studied the crystal structure at room temperature and low temperature, as well as the magnetoresi...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The crystal and magnetic structure of (La0.70Ca0.30)(CryMn1-y)O3 for y = 0.70, 0.50 and 0.15 has bee...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The magnetic properties of La1-σMnO3 depend on the relative concentration of Mn+4/Mn+3 introduced by...
THE EFFECT OFCu-DOPINGON CRYSTAL STRUCTURE AND MAGNETORESISTANCE IN La0.73 Ca0.27 Mn1-y CuyO3 WITH 0...
THE EFFECT OFCu-DOPINGON CRYSTAL STRUCTURE AND MAGNETORESISTANCE IN La0.73 Ca0.27 Mn1-y CuyO3 WITH 0...
THE STRUCTURAL AND MAGNETIC PROPERTIES OF La1-xCaxMnO3WITH x = 0.27 AND 0.47. We have studied the st...
THE STRUCTURAL AND MAGNETIC PROPERTIES OF La1-xCaxMnO3WITH x = 0.27 AND 0.47. We have studied the st...
The La1-xCaxMnO3 series of compounds with antiferromagnetic ground states (x≥1/2) have been extensiv...
We studied the crystal and magnetic structure of the La1 xCaxMnO3 compound for 0.11 lt;or x lt;or 0...
The crystal and magnetic structures of La0.70Ca0.30CryMn1 12yO3 for y=0.70, 0.50, and 0.15 have been...
We studied the crystal structure at room temperature and low temperature, as well as the magnetoresi...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The crystal and magnetic structure of (La0.70Ca0.30)(CryMn1-y)O3 for y = 0.70, 0.50 and 0.15 has bee...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The crystal and magnetic structures of (La0.70Ca0.30)(CryMn1−y)O3 for y=0.70, 0.50, and 0.15 h...
The magnetic properties of La1-σMnO3 depend on the relative concentration of Mn+4/Mn+3 introduced by...
THE EFFECT OFCu-DOPINGON CRYSTAL STRUCTURE AND MAGNETORESISTANCE IN La0.73 Ca0.27 Mn1-y CuyO3 WITH 0...
THE EFFECT OFCu-DOPINGON CRYSTAL STRUCTURE AND MAGNETORESISTANCE IN La0.73 Ca0.27 Mn1-y CuyO3 WITH 0...
Add to ORKG