Engineering of dislocation-loops for light emission from silicon diodes

Luminescence properties of silicon light emitting diodes with engineered dislocation loops were investigated. Dislocation loops were formed by Si+-ion implantation above and below metallurgical p+-n junction followed by an annealing step. The diodes showed characteristic dislocation (D-band) and band-to-band luminescence. Measurements of carrier-injection level dependence of the D-band signal intensity were performed. The results are in agreement with the model for dislocation luminescence, which suggests rediative transition between two, dislocation-related shallow levels. A gradual blue-shift of the D-band peak positions was observed with an increase in the carrier injection level in electroluminescence and photoluminescence. A supposition about existence of strong Stark effect for the excitonic dislocation states allows explaining the observations. Namely, in the build-in electric field of the p-n junction the exciton energies are red-shifted. The injected charge carriers lower the field and thus cause the blue-shift of the peak positions. A fitting of the data using the quadratic Stark effect equation suggests 795 meV for the spectral position of D1 peak at 300 K and 0.0186 meV/(kV/cm)2 for the characteristic constant