Minimizing Fabrication Time Of Calcium Modified Pbti03 Nanoceramics By HEBM Technique

Lead titanate is one of the family member of ABO3 structure perovskite having piezoelectric as well as pyroelectric properties in nature. It shows highl ferroelectric property as ceramic materials. Ca modified lead titanate termed as P1-xCXT synthesized by HEBM at 270 C of room temperature. The stoichiometric ratio was taken as Pb1-xCaxTi03 where Ca0 was taken in various ratio . Structural and electrical properties were studied by taking measurement with standard instruments LCR metre. Analysis of XRD gives that doping of calcium produce a decrease in tetragonal size and hence the volume . As a result on A-site substitution observed. Graph of electrical parameters shows that impedence decreases exponentially with frequency