Evaluation and auger analysis of a zinc-dialkyl-dithiophosphate antiwear additive in several diester lubricants

The wear of pure iron in sliding contact with hardened M-2 tool steel was measured for a series of synthetic diester fluids, both with and without a zinc dialkyl dithiophosphate (ZDP) antiwear additive, as test lubricants. Selected wear scars were analyzed by an Auger emission spectroscopy (AES) depth profiling technique in order to assess the surface film elemental composition. The ZDP was an effective antiwear additive for all the diesters except dibutyl oxalate and dibutyl sebacate. The high wear measured for the additive-containing oxalate was related to corrosion; the higher wear measured for the additive-containing sebacate was due to an oxygen interaction. The AES of dibutyl sebacate surfaces run in dry air and in dry nitrogen showed large differences only in the amount of oxygen present. The AES of worn surfaces where the additive was effective showed no zinc, only a little phosphorus, and large amounts of sulfur