Investigation on the strain behaviour of a precipitation-hardenable aluminium alloy through a temperature gradient based heat treatment

In this work the strain behaviour of the heat-treated 6xxx series aluminium alloy AC170PX is investigated by a not conventional approach. Thanks to the low density combined with good mechanical properties, this aluminium alloy is often adopted for automotive applications. Despite these advantages, its formability at room temperature is low. In order to overcome this limit, a distribution of the material properties can be achieved by a local heat treatment (Tailored Heat Treated Blanks). In this context, to evaluate the effects of those parameters mainly affecting the precipitation hardening (aging temperature and aging time), a first experimental campaign was conducted using conventional furnace heat treatment in different conditions . Tensile tests were run with the aim of determining the flow and the aging curves of the heat treated specimens. Starting from these results, a not uniform heat treatment was designed using a Gleeble physical simulator Heat treatments based on a temperature gradient along the sample were performed. Then, tensile tests of the so heated specimens were carried out at room temperature. Through a digital image correlation system both the distribution and the evolution of the strain along the gauge length of the specimen were analysed in order to obtain the hardening/softening working conditions related to a specific heating cycle. These results were validated by the comparison with the data obtained from the first experimental campaign