Contains fulltext : 169646.pdf (publisher's version ) (Closed access)OBJECTIVES: Composite resin restorations present high survival rates and when a failure occurs repair is often possible. The aim of this study was to assess the effect of various repair techniques on indirect restorations. METHODS: LAVA Ultimate (3M), and Clearfil Estenia blocks (Kuraray) were repaired with our without surface roughness treatments, silane application and artificial ageing. Micro-shear bond stress tests were performed, while cohesive strength served as positive control. ANOVA was used for cohesive strength and effect of ageing, and linear mixed models to evaluate the effect of treatment variables on repair strength. RESULTS: Both materials...
This study evaluated the effect of surface conditioning methods and adhesive systems on the repair b...
WOS: 000294079200008PubMed ID: 20978641Purpose: To evaluate the effect of different surface treatmen...
Purpose: To assess the impact of different surface treatments on the push-out bond strength between ...
OBJECTIVES: Composite resin restorations present high survival rates and when a failure occurs repai...
Purpose: To evaluate the tensile bond strength of indirect composites repaired with different surfac...
Purpose: This study evaluated the effect of surface conditioning methods and thermocycling on the bo...
Purpose: This study evaluated the effect of different physicochemical aging methods and surface cond...
AbstractIntroduction: Sometimes repair of indirect composite restorations is preferable to replaceme...
This study evaluated the effect of surface conditioning methods on the microtensile bond strength (µ...
OBJECTIVES: The aim of this study was to investigate the effectiveness of a variety of techniques to...
Statement of the Problem: An adequate repair procedure depends on high bond strength between the exi...
The use of resin-based composite materials in operative dentistry is increasing, including applicati...
Objectives: Despite over 40-years of clinical use there are still no clear guidelines on what pre-tr...
Purpose: To evaluate the tensile bond strength at repaired interfaces of aged dental composites, eit...
Objective: Repair of an indirect restoration is usually preferred over its replacement. This study a...
This study evaluated the effect of surface conditioning methods and adhesive systems on the repair b...
WOS: 000294079200008PubMed ID: 20978641Purpose: To evaluate the effect of different surface treatmen...
Purpose: To assess the impact of different surface treatments on the push-out bond strength between ...
OBJECTIVES: Composite resin restorations present high survival rates and when a failure occurs repai...
Purpose: To evaluate the tensile bond strength of indirect composites repaired with different surfac...
Purpose: This study evaluated the effect of surface conditioning methods and thermocycling on the bo...
Purpose: This study evaluated the effect of different physicochemical aging methods and surface cond...
AbstractIntroduction: Sometimes repair of indirect composite restorations is preferable to replaceme...
This study evaluated the effect of surface conditioning methods on the microtensile bond strength (µ...
OBJECTIVES: The aim of this study was to investigate the effectiveness of a variety of techniques to...
Statement of the Problem: An adequate repair procedure depends on high bond strength between the exi...
The use of resin-based composite materials in operative dentistry is increasing, including applicati...
Objectives: Despite over 40-years of clinical use there are still no clear guidelines on what pre-tr...
Purpose: To evaluate the tensile bond strength at repaired interfaces of aged dental composites, eit...
Objective: Repair of an indirect restoration is usually preferred over its replacement. This study a...
This study evaluated the effect of surface conditioning methods and adhesive systems on the repair b...
WOS: 000294079200008PubMed ID: 20978641Purpose: To evaluate the effect of different surface treatmen...
Purpose: To assess the impact of different surface treatments on the push-out bond strength between ...