Effect of homogeneous ceramic tile waste on properties of mortar

The subject of reduce, reuse and recycle of waste material either from industrial or agricultural sectors is considered very important in the general attempt for sustainable construction. In relation to that, ceramic materials are widely used in many part of the world and consequently, large quantities of wastes are produced simultaneously by brick and tile manufacturers and construction industry. However, part of these wastes and those produced by the construction industry are dumped in landfills. In this present research, the effect of homogeneous ceramic tile waste on harden properties of mortar was investigated. Mortar mixes were prepared focusing on the effect of ceramic aggregates as river sand replacement. Tests were conducted for compressive strength, splitting tensile strength for all mortar specimens. The cement was partially replaced by ceramic powder by 20 %, 40 % and 60 %, respectively by weight of cement. The sand was replaced by ceramic aggregates ranging from 0% to 100% by weight of aggregates. The size of ceramic aggregates used is modified in accordance with ASTM C-33 while the cement was partially replaced by 40 % of ceramic powder by weight of cement. All specimens were cast in 50 mm cubes and cured in water after demoulding until the age of testing. By replacing 100 % of sand with ceramic aggregates, it was found that the compressive strength was very much similar to the control specimen without showing any negative effect. Similarly, by replacing cement with ceramic powder, the strength of mortar shows 10% increment as compared to control specimen. In conclusion, incorporation of homogenous ceramic tile waste either as sand replacement or cement replacement both can enhance the properties of mortar in fresh and hardened states