Structural effects in UO2 thin films irradiated with fission-energy Xe ions

AbstractUranium dioxide thin films have been successfully grown on LSAT (Al10La3O51Sr14Ta7) substrates by reactive magnetron sputtering. Irradiation by 92 MeV 129Xe23+ ions to simulate fission damage that occurs within nuclear fuels caused microstructural and crystallographic changes. Initially flat and continuous thin films were produced by magnetron sputtering with a root mean square roughness of 0.35 nm determined by AFM. After irradiation, this roughness increased to 60–70 nm, with the films developing discrete microstructural features: small grains (∼3 μm), along with larger circular (up to 40 μm) and linear formations with non-uniform composition according to the SEM, AFM and EDX results. The irradiation caused significant restructuring of the UO2 films that was manifested in significant film-substrate mixing, observed through EDX analysis. Diffusion of Al from the substrate into the film in unirradiated samples was also observed