AbstractA quenched and tempered high strength low alloy steel NIONIKRAL 70 for producing welded pressure vessels, where high resistance to fatigue crack propagation and high tolerance of damage are of high importance, has been investigated. Low cycle fatigue tests were conducting on several series of uniaxial cylindrical smooth specimens under strain control. The cycle behavior of the material is characterized using Coffin-Manson relation
Group of high strength low alloy steel, signs NIONIKRAL60 and NIONIKRAL70, created as the need to re...
In this work is tested applicability of the extended uniform material law for high-strength steel o...
In view of the importance of high strength low alloy (HSLA) steels, particularly for critical applic...
A quenched and tempered high strength low alloy steel NIONIKRAL 70 for producing welded pressure ves...
AbstractA quenched and tempered high strength low alloy steel NIONIKRAL 70 for producing welded pres...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. Cycle loading of mat...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of mat...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of mat...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of mat...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. Cycle loading of mat...
Experimental research on the behaviour of high-strength low-alloy steel ( HSLA)exposed to low-cycle ...
The cycle loading of a material results in the modification of its properties and so in this paper i...
In present paper, the experimental research of the behaviour of high-strength low-alloy steel (HSLA)...
Group of high strength low alloy steel, signs NIONIKRAL60 and NIONIKRAL70, created as the need to re...
From a fracture mechanics point of view on welded joints, it is assumed that the welded joint is pre...
Group of high strength low alloy steel, signs NIONIKRAL60 and NIONIKRAL70, created as the need to re...
In this work is tested applicability of the extended uniform material law for high-strength steel o...
In view of the importance of high strength low alloy (HSLA) steels, particularly for critical applic...
A quenched and tempered high strength low alloy steel NIONIKRAL 70 for producing welded pressure ves...
AbstractA quenched and tempered high strength low alloy steel NIONIKRAL 70 for producing welded pres...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. Cycle loading of mat...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of mat...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of mat...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of mat...
Low cycle fatigue test was performed in ambient atmosphere at room temperature. Cycle loading of mat...
Experimental research on the behaviour of high-strength low-alloy steel ( HSLA)exposed to low-cycle ...
The cycle loading of a material results in the modification of its properties and so in this paper i...
In present paper, the experimental research of the behaviour of high-strength low-alloy steel (HSLA)...
Group of high strength low alloy steel, signs NIONIKRAL60 and NIONIKRAL70, created as the need to re...
From a fracture mechanics point of view on welded joints, it is assumed that the welded joint is pre...
Group of high strength low alloy steel, signs NIONIKRAL60 and NIONIKRAL70, created as the need to re...
In this work is tested applicability of the extended uniform material law for high-strength steel o...
In view of the importance of high strength low alloy (HSLA) steels, particularly for critical applic...