Martensite structures and twinning in substrate-constrained epitaxial Ni–Mn–Ga films deposited by a magnetron co-sputtering process

AbstractIn order to obtain Ni–Mn–Ga epitaxial films crystallized in martensite structures showing Magnetic-Induced Rearrangement (MIR) of martensite variants, a fine control of the composition is required. Here we present how the co-sputtering process might be helpful in the development of Ni–Mn–Ga epitaxial films. A batch of epitaxial Ni–Mn–Ga films deposited by co-sputtering of a Ni-Mn-Ga ternary target and a pure manganese target has been studied. The co-sputtering process allows a precise control of the film compositions and enables keeping the epitaxial growth of Ni-Mn-Ga austenite during deposition at high temperature. It gives rise to tune the content of the MIR-active 14-modulated martensite in the film at room temperature, as well as micro and macro-twinned domains sizes