Multiscale and multimodality computed tomography for cortical bone analysis

International audienceIn clinical studies, high resolution peripheral quantitative computed tomography (HR-pQCT) is used to separately evaluate cortical bone and trabecular bone with an isotropic voxel of 82 µm3, and typical cortical parameters are cortical density (D.comp), thickness (Ct.Th), and porosity (Ct.Po).In vitro, micro-computed tomography (micro-CT) is used to explore the internal cortical bone micro-structure with isotropic voxels and high resolution synchrotron radiation (SR); micro-CT is considered the 'gold standard'.In 16 tibias and 8 femurs, HR-pQCT measurements were compared to conventional micro-CT measurements. To test modality effects, conventional micro-CT measurements were compared to SR micro-CT measurements at 7.5 µm3; SR micro-CT measurements were also tested at different voxel sizes for the femurs, specifically, 7.5 µm3 versus 2.8 µm3.D.comp (r = −0.88, p < 10−3) was the parameter best correlated with porosity (Po.V/TV). The correlation was not affected by the removal of pores under 130 µm. Ct.Th was also significantly highly correlated (r = −0.89 p < 10−3), while Ct.Po was correlated with its counterpart Po.V/TV (r = 0.74, p < 10−3).From SR micro-CT and conventional micro-CT at 7.5 µm3 in matching areas, Po.V/TV and pore diameter were underestimated in conventional micro-CT with mean ± standard deviation (SD) biases of −2.5 ± 1.9% and −0.08 ± 0.08 mm, respectively. In contrast, pore number (Po.N) and pore separation (Po.Sp) were overestimated with mean ± SD biases of +0.03 ± 0.04 mm−1 and +0.02 ± 0.04 mm, respectively. The results from the tibia and femur were similar when the results of SR micro-CT at 7.5 µm3 and 2.8 µm3 were compared. Po.V/TV, specific surface of pores (Po.S/Po.V), and Po.N were underestimated with mean biases of −1.7 ± 0.9%, −4.6 ± 4.4 mm−1, and −0.26 ± 0.15 mm−1, respectively. In contrast, pore spacing was overestimated at 7.5 µm3 compared to 2.8 µm3 with mean biases of 0.05 ± 0.03 mm.Cortical bone measurements from HR-pQCT images provided consistent results compared to those obtained using conventional micro-CT at the distal tibia. D.comp was highly correlated to Po.V/TV because it considers both the micro-porosity (Haversian systems) and macro-porosity (resorption lacunae) of cortical bone. The complexity of canal organization, (including shape, connectivity, and surface) are not fully considered in conventional micro-CT in relation to beam hardening and cone beam reconstruction artifacts. With the exception of Po.V/TV measurements, morphological and topological measurements depend on the characteristics of the x-ray beam, and to a lesser extent, on image resolution