Add to ORKGThis paper explores the impact of tribocorrosion wear caused by an aggressive acidic media. Tests were conducted on samples made of stainless steel AISI 316L, 304L and 440C. Austenitic steels were tested in their nitrided state and martensitic in quenched and tempered and then induction hardened state. Electrochemical corrosion resistance testing and analysis of the microstructure and hardness in the cross section was carried out on samples of selected steels. To test the possibility of applying surface modification of selected materials in conditions of use, tests were conducted on samples/parts in a worm press for final pressing
Nanopeening treatment was applied to the AISI 420 steel to decrease its sensitivity to tribocorrosio...
La présente thèse doctorale vise à analyser le comportement tribologique, en corrosion et en triboco...
Tribocorrosion is a term used to describe the material degradation due to the combination of electro...
This paper explores the impact of tribocorrosion wear caused by an aggressive acidic media. Tests we...
Analyzed was the influence of tribocorrosion wear due to effects of fatty acids present in the proce...
Abstract: In this paper the tribocorrosion behaviours of AISI 310 and AISI 316 stainless steels have...
The tribo-electrochemical behavior of two new martensitic stainless steels in a 3% NaCI solution has...
In this study, types 440B (martensitic) and 304 (austenitic) stainless steel were subjected to micro...
Tribocorrosion is one of the most dangerous threats to material systems due to the accelerated and u...
Tribocorrosion is defined as the chemical-electrochemical-mechanical process leading to a degradatio...
Tribocorrosion has been studied for many years by electrochemists as well as by tribologists, using ...
DIN 1.4110 martensitic stainless steel is largely used in the cutlery industry due to its high corro...
Austenitic stainless steels are prone to galling and seizure in sliding contacts and display poor re...
Tribocorrosion is a poorly understood material degradation process where wear and corrosion processe...
Stainless steel is widely used as dental implant. However, there has been little work on the micro-a...
Nanopeening treatment was applied to the AISI 420 steel to decrease its sensitivity to tribocorrosio...
La présente thèse doctorale vise à analyser le comportement tribologique, en corrosion et en triboco...
Tribocorrosion is a term used to describe the material degradation due to the combination of electro...
This paper explores the impact of tribocorrosion wear caused by an aggressive acidic media. Tests we...
Analyzed was the influence of tribocorrosion wear due to effects of fatty acids present in the proce...
Abstract: In this paper the tribocorrosion behaviours of AISI 310 and AISI 316 stainless steels have...
The tribo-electrochemical behavior of two new martensitic stainless steels in a 3% NaCI solution has...
In this study, types 440B (martensitic) and 304 (austenitic) stainless steel were subjected to micro...
Tribocorrosion is one of the most dangerous threats to material systems due to the accelerated and u...
Tribocorrosion is defined as the chemical-electrochemical-mechanical process leading to a degradatio...
Tribocorrosion has been studied for many years by electrochemists as well as by tribologists, using ...
DIN 1.4110 martensitic stainless steel is largely used in the cutlery industry due to its high corro...
Austenitic stainless steels are prone to galling and seizure in sliding contacts and display poor re...
Tribocorrosion is a poorly understood material degradation process where wear and corrosion processe...
Stainless steel is widely used as dental implant. However, there has been little work on the micro-a...
Nanopeening treatment was applied to the AISI 420 steel to decrease its sensitivity to tribocorrosio...
La présente thèse doctorale vise à analyser le comportement tribologique, en corrosion et en triboco...
Tribocorrosion is a term used to describe the material degradation due to the combination of electro...