Degradation Mechanisms of Heat Resistant Steel at Elevated Temperatures : In an Iron Ore Pelletizing Industry

This thesis focuses on the different degradation mechanisms of the stainless steel in a travelling grate in a Grate-Kiln iron ore pellet indurator. The travelling grate is a conveyor belt that transports green-body pellets to a rotary kiln while the pellets are being dried and pre-heated to a temperature of 900-1100 °C by recycled hot air. After unloading of the pellets to the rotary-kiln for further sintering, the travelling grate is cooled in room temperature while returning to the loading zone of the wet pellets. The steel was tested during thermal cycling in a test-rig, in order to simulate the influence of thermo mechanical fatigue and oxide spallation. The influence of erosion-deposition was investigated in a modified horizontal industrial combustion kiln at 800 °C, with slag and coal from production used as erosive media and combustion fuel, respectively. The influence of minor alloying additions of Mn, Si and Ti on the microstructure was explored by eight different casted alloy compositions. Isothermal heat treatments were performed at 800 °C during 200 hours on steel immersed in deposits recovered from a travelling grate in production. The three main degradation mechanisms found in this work are thermal spallation, erosion-deposition and deposit induced accelerated corrosion (DIAC). Thermal spallation of the oxide layer is caused by the thermal expansion difference between the oxide and the metal during heating and cooling. It has been found that Ti improves the spallation resistance while Si reduces it. Spallation of deposits is another cause believed to increase the degradation. Erosion-deposition appears due to simultaneous erosion and deposition of particles on the travelling grate that causes erosion or deposition depending on the amount of alkali metals in the environment. The velocity of the particles also influences erosion and deposition in the way that higher velocities increase erosion. DIAC is proposed to form on the travelling grate due to the concentration of chloride- and sulphate containing alkali metals in the deposits. Other than these major degrading mechanisms, minor degradation mechanisms such as internal oxidation, sigma formation, carburization and sensitization towards inter-granular attack have been found inside the steel during heating. Thermo mechanical fatigue (TMF) causes intergranular cracks in the material of the travelling grate. Casting issues such as micro-segregation have also been addressed in this thesis. A few different ways to improve degradation resistance have been proposed, such as homogenization heat treatments, optimization of process parameters and inhibitor solutions.