The formation of powder materials based on nickel aluminide using technology of spark plasma sintering VKNA and PN85YU15 powders

Structure and mechanical properties of materials based on Ni3Al intermetallic sintered using two types of powders «VKNA» and «PN85Yu15» were investigated. Sintering of materials was performed using spark plasma sintering technology under equal conditions for both materials. The bending strength of material sintered using «PN85Yu15» powder was 890 MPa, material sintered using «VKNA» powder showed the strength level about 330 MPa. Low values of «VKNA» alloy strength level can be explained by high porosity (20 %) of the material due to the presence of refractory elements in the initial powder.Проведено сравнительное исследование структуры и механических свойств материалов на основе интерметаллида Ni3Al двух типов – ВКНА и ПН85Ю15, полученных с использованием технологии искрового плазменного спекания порошков при одинаковых условиях. Предел прочности при изгибе спечённого порошка ПН85Ю15 составляет 890 МПа, спечённого порошка ВКНА – 330 МПа. Низкие значения прочности сплава ВКНА, спечённого при данных режимах, объясняются повышенной пористостью (20 %) материала из-за наличия тугоплавких элементов в составе исходного порошка.Работа была выполнена при финансовой поддержке Российского Фонда Фундаментальных Исследований (проект 15-33-50845)