The influence of nanostructuring frictional treatment on the tribological properties of austenitic chromium-nickel steel

The influence of nanostructuring frictional treatment by diamond indenter on phase composition, structure, micromechanical and tribological characteristics of austenitic 12Kh18N10T steel surface layers was studied. It was established that frictional treatment forms quality surface with low value of roughness parameter. At that, high level of surface hardening, essential decrease of wear rate and friction coefficient under conditions of dry sliding friction is achieved. Increased ability of nanostructured layer to resist to plastic deformation was educed.Изучено влияние наноструктурирующей фрикционной обработки индентором из синтетического алмаза на фазовый состав, структуру, микромеханические и трибологические характеристики поверхностных слоев аустенитной стали 12Х18Н10Т. Установлено, что при фрикционной обработке формируется качественная поверхность с низким значением параметра шероховатости. При этом достигается высокий уровень упрочнения поверхности, существенное снижение интенсивности изнашивания и коэффициента трения в условиях сухого трения скольжения. Выявлена повышенная способность наноструктурированного слоя сопротивляться пластическому деформированию.Работа выполнена по теме «Структура» № 01201463331 (проект № 15-9-12-45) при поддержке РФФИ (проект № 15-08-07947). Трибологические и микромеханические испытания, электронная сканирующая микроскопия и профилометрия выполнены в ЦКП «Пластометрия» ИМАШ УрО РАН. Электронная просвечивающая микроскопия реализована на оборудовании Лаборатории структурных методов анализа материалов и наноматериалов ЦКП УрФУ