Mechanical and magnetic properties of high-nitrogen austenitic steel (HNS) 06H18AG19M2

Submitted by investigating the mechanical properties of focused bend testing of High-nitrogen austenitic steel (HNS) 06H18AG19M2 in air and 3.5% NaCl aqueous solution after hardening from 1150 °C, subsequent aging at 500 and 800 °C and equal channel angular pressing (ECAP) with different degrees of deformation. Also the studies of magnetic properties were conducted after different structural states of steel. It is shown that the steel is paramagnetic regardless of the mode of its processing, the exception is a state after quenching from 1200 ° C, when detected significant spontaneous magnetization of steel in an external magnetic field.Выполнены исследования механических свойств путем испытаний на сосредоточенный изгиб высокоазотистой аустенитной стали (ВАС) 06Х18АГ19М2 на воздухе и в 3,5%-ном водном растворе NaCl после закалки от 1150 °С, последующего старения при 500 и 800 °С, а также равноканального углового прессования (РКУП) с различными степенями деформации. Также проведены магнитные исследования стали в различных структурных состояниях. Показано, что сталь остается парамагнитной независимо от режима обработки, исключение составляет состояние после закалки от 1200 °С, когда обнаруживается значительная спонтанная намагниченность стали во внешнем магнитном поле