Add to ORKGHigh temperature tests to determine fatigue life of 120mm bore ball bearings with fluorocarbon, polyphenyl ether, and synthetic base paraffin base lubricant
The operating characteristics of large diameter rolling-element bearings in the ultra high speed reg...
Steel friction and wear tests in nitrogen with paraffinic resins, synthetic paraffinic oil, glycol, ...
Test apparatus for evaluation of high temperature lubricants to 1500 deg F and greases to 600 deg F ...
High temperature fatigue tests of steel ball bearings with synthetic paraffinic oil lubricant in low...
Synthetic paraffinic oil lubricates ball bearings at temperatures in the 600 degrees F range. The lu...
Groups of 120-mm-bore angular-contact ball bearings made from AISI M-50 steel were fatigue tested wi...
Rolling contact bearing torque measurements and fatigue life tests of high temperature lubricant
Rolling-element fatigue tests were run with three synthetic lubricants with and without antiwear add...
Calcium fluoride-barium fluoride coating on ball bearing cages or as fillers in porous bearing cages...
Test evaluation of high temperature greases and solid lubricants in thrust loaded ball bearing
Rolling-element fatigue and lubrication with fluorinated polyethers at cryogenic temperature
Surface pitting fatigue life tests were conducted with five lubricants, using spur gears made from a...
Bearing life tests in vacuum with three space liquid lubricants, two multiply alkylated cyclopentane...
Rolling contact lubrication characteristics of polyphenyl ethers and mineral oils at reduced pressur...
AISI 52100, a high carbon chromium steel, has the longest fatigue life of eight bearing materials te...
The operating characteristics of large diameter rolling-element bearings in the ultra high speed reg...
Steel friction and wear tests in nitrogen with paraffinic resins, synthetic paraffinic oil, glycol, ...
Test apparatus for evaluation of high temperature lubricants to 1500 deg F and greases to 600 deg F ...
High temperature fatigue tests of steel ball bearings with synthetic paraffinic oil lubricant in low...
Synthetic paraffinic oil lubricates ball bearings at temperatures in the 600 degrees F range. The lu...
Groups of 120-mm-bore angular-contact ball bearings made from AISI M-50 steel were fatigue tested wi...
Rolling contact bearing torque measurements and fatigue life tests of high temperature lubricant
Rolling-element fatigue tests were run with three synthetic lubricants with and without antiwear add...
Calcium fluoride-barium fluoride coating on ball bearing cages or as fillers in porous bearing cages...
Test evaluation of high temperature greases and solid lubricants in thrust loaded ball bearing
Rolling-element fatigue and lubrication with fluorinated polyethers at cryogenic temperature
Surface pitting fatigue life tests were conducted with five lubricants, using spur gears made from a...
Bearing life tests in vacuum with three space liquid lubricants, two multiply alkylated cyclopentane...
Rolling contact lubrication characteristics of polyphenyl ethers and mineral oils at reduced pressur...
AISI 52100, a high carbon chromium steel, has the longest fatigue life of eight bearing materials te...
The operating characteristics of large diameter rolling-element bearings in the ultra high speed reg...
Steel friction and wear tests in nitrogen with paraffinic resins, synthetic paraffinic oil, glycol, ...
Test apparatus for evaluation of high temperature lubricants to 1500 deg F and greases to 600 deg F ...