Add to ORKGStress corrosion cracking susceptibility of titanium alloys in nitrogen tetroxide and aqueous and hot salt environment
In an effort to simulate typical compressor operating conditions of current turbine engines, special...
Stress corrosion cracking of titanium aluminum vanadium alloy in nitrogen tetroxide under pressur
The influence of exposure cycle on the hot-salt stress-corrosion cracking resistance of the Ti-8Al-1...
Metal composition effects on stress corrosion cracking of titanium alloys in nitrogen tetroxide, wat...
This report investigates stress corrosion cracking susceptibility of titanium alloys in nitrogen tet...
Stress corrosion data for titanium alloys in aqueous, hot salt, and nitrogen dioxide environment
A detailed study was made of the relation between the size distribution of Ti3Al particles in a Ti-8...
Emphasis has been placed on determining the interrelations among the composition, phase structure, d...
Stress corrosion cracking tests of titanium alloys at ambient temperature in aqueous solution
Susceptibility of titanium alloys to hot-salt stress-corrosion cracking increased as follows: Ti-2Al...
Stress corrosion tests of titanium alloys in distilled and aqueous salt solutions at ambient tempera...
Aluminum concentration effects on stress corrosion cracking of titanium alloys at ambient temperatur...
Hot salt stress corrosion cracking of titanium aluminum alloys in presence of anhydrous hydrogen chl...
Stress corrosion cracking of titanium alloys at ambient temperature in aqueous solution
Aluminum concentration effects on stress corrosion cracking of titanium alloys in aqueous solution
In an effort to simulate typical compressor operating conditions of current turbine engines, special...
Stress corrosion cracking of titanium aluminum vanadium alloy in nitrogen tetroxide under pressur
The influence of exposure cycle on the hot-salt stress-corrosion cracking resistance of the Ti-8Al-1...
Metal composition effects on stress corrosion cracking of titanium alloys in nitrogen tetroxide, wat...
This report investigates stress corrosion cracking susceptibility of titanium alloys in nitrogen tet...
Stress corrosion data for titanium alloys in aqueous, hot salt, and nitrogen dioxide environment
A detailed study was made of the relation between the size distribution of Ti3Al particles in a Ti-8...
Emphasis has been placed on determining the interrelations among the composition, phase structure, d...
Stress corrosion cracking tests of titanium alloys at ambient temperature in aqueous solution
Susceptibility of titanium alloys to hot-salt stress-corrosion cracking increased as follows: Ti-2Al...
Stress corrosion tests of titanium alloys in distilled and aqueous salt solutions at ambient tempera...
Aluminum concentration effects on stress corrosion cracking of titanium alloys at ambient temperatur...
Hot salt stress corrosion cracking of titanium aluminum alloys in presence of anhydrous hydrogen chl...
Stress corrosion cracking of titanium alloys at ambient temperature in aqueous solution
Aluminum concentration effects on stress corrosion cracking of titanium alloys in aqueous solution
In an effort to simulate typical compressor operating conditions of current turbine engines, special...
Stress corrosion cracking of titanium aluminum vanadium alloy in nitrogen tetroxide under pressur
The influence of exposure cycle on the hot-salt stress-corrosion cracking resistance of the Ti-8Al-1...