Add to ORKGSixty-eight high temperature Co-, Fe-, and Ni-base alloys were tested for 10-one thousand hour cycle...
Oxidation of nickel alloys determined by X ray diffraction, weight and thickness change measurements...
The Ni-base superalloys are a popular range of materials for study following consolidation by additi...
Investigating effect of surface preparation on oxidation of WI-52 by high temperature X ray diffract...
"High-temperature X-ray diffraction, high-temperature microscopy, and weight-gain experiments were c...
Oxidation resistance determined for cobalt and nickel based alloys by isothermal and cyclic tests in...
The oxidation at 900 and 1,000 C of four nickel-base superalloys in 1 atmosphere of slowly flowing o...
Examination of thermal oxidation deposits on heat resistant alloys using X ray diffraction and X ray...
Three oxidation-resistant alloy foil claddings for protecting typical gas turbine engine alloys of n...
The initial study reported here focused on the oxidation of Co-Al-W alloys containing nickel (29-34 ...
High temperature oxidation causes degradation of materials in aircraft, marine, industrial and land ...
This first in a series of cyclic oxidation handbooks contains specific-weight-change-versus-time dat...
Research on the high temperature oxidation and Na2SO4 induced hot corrosion of some nickel base supe...
The present investigation was conducted to study the oxidation kinetics of nickel-based superalloy 2...
Volatilization of oxides during cyclic oxidation of commercial Nichrome, Inconel 750, Rene 41, Stell...
Sixty-eight high temperature Co-, Fe-, and Ni-base alloys were tested for 10-one thousand hour cycle...
Oxidation of nickel alloys determined by X ray diffraction, weight and thickness change measurements...
The Ni-base superalloys are a popular range of materials for study following consolidation by additi...
Investigating effect of surface preparation on oxidation of WI-52 by high temperature X ray diffract...
"High-temperature X-ray diffraction, high-temperature microscopy, and weight-gain experiments were c...
Oxidation resistance determined for cobalt and nickel based alloys by isothermal and cyclic tests in...
The oxidation at 900 and 1,000 C of four nickel-base superalloys in 1 atmosphere of slowly flowing o...
Examination of thermal oxidation deposits on heat resistant alloys using X ray diffraction and X ray...
Three oxidation-resistant alloy foil claddings for protecting typical gas turbine engine alloys of n...
The initial study reported here focused on the oxidation of Co-Al-W alloys containing nickel (29-34 ...
High temperature oxidation causes degradation of materials in aircraft, marine, industrial and land ...
This first in a series of cyclic oxidation handbooks contains specific-weight-change-versus-time dat...
Research on the high temperature oxidation and Na2SO4 induced hot corrosion of some nickel base supe...
The present investigation was conducted to study the oxidation kinetics of nickel-based superalloy 2...
Volatilization of oxides during cyclic oxidation of commercial Nichrome, Inconel 750, Rene 41, Stell...
Sixty-eight high temperature Co-, Fe-, and Ni-base alloys were tested for 10-one thousand hour cycle...
Oxidation of nickel alloys determined by X ray diffraction, weight and thickness change measurements...
The Ni-base superalloys are a popular range of materials for study following consolidation by additi...