Structure and properties of porous ceramics obtained from aluminum hydroxide

In this paper the study of porous ceramics obtained from aluminum hydroxide with gibbsite modification is presented. The dependence of porosity and mechanical characteristics of the material sintered at different temperatures was studied. It was shown that compressive strength of alumina ceramics increases by 40 times with decreasing the pore volume from 65 to 15%. It was shown that aluminum hydroxide may be used for pore formation and pore volume in the sintered ceramics can be controlled by varying the aluminum hydroxide concentration and sintering temperature. Based on these results one can conclude that the obtained structure is very close to inorganic bone matrix and can be used as promising material for bone implants production