Beads, beaded-fibres and fibres: Tailoring the morphology of poly(caprolactone) using pressurised gyration

This work focuses on forming bead on string poly(caprolactone) (PCL) by using gyration under pressure. The fibre morphology of bead on string is an interesting feature that falls between bead-free fibres and droplets, and it could be effectively controlled by the rheological properties of spinning dopes and the major processing parameters of the pressurised gyration system which are working pressure and rotating speed. Bead products were not always spherical in shape and tended to be more elliptical, therefore both their width and length were measured. The average bead width and length produced spanned a range 145-660μm and 140-1060μm, respectively. The average distance between two adjacent beads (i.e. inter-bead distance) and the bead size (width and length) are shown to be a function of processing parameters and polymer concentration. An interesting morphology i.e. beads with short fibre was observed when using a high polymer concentration. Bead on string structure agglomeration was promoted by a low polymer concentration. Formation of droplets or agglomerated bead on string is promoted below 5wt% polymer concentration, and beads with short fibre were present in the microstructure beyond a polymer concentration of 20wt%