The Use of C-MnO2 as Hybrid Precursor Support for a Pt/C-MnxO1+x Catalyst with Enhanced Activity for the Methanol Oxidation Reaction (MOR)

Platinum (Pt) nanoparticles are deposited on a hybrid support (C-MnO2) according to a polyol method. The home-made catalyst, resulted as Pt/C-MnxO1+x, is compared with two different commercial platinum based materials (Pt/C and PtRu/C). The synthesized catalyst is characterized by means of FESEM, XRD, ICP-MS, XPS and μRS analyses. MnO2 is synthesized and deposited over a commercial grade of carbon (Vulcan XC72) by facile reduction of potassium permanganate in acidic solution. Pt nanoparticles are synthesized on the hybrid support by a polyol thermal assisted method (microwave irradiation), followed by an annealing at 600 °C. The obtained catalyst displays a support constituted by a mixture of manganese oxides (Mn2O3 and Mn3O4) with a Pt loading of 19 wt. %. The electro-catalytic activity towards MOR is assessed by RDE in acid conditions (0.5 M H2SO4), evaluating the ability to oxidize methanol in 1 M concentration. The synthesized Pt/C-MnxO1+x catalyst shows good activity as well as good stability compared to the commercial Pt/C based catalyst