Tellurium precipitates in (Cd,Mn)Te:V crystals: Effects of annealing

We suggest that (Cd,Mn)Te is a suitable material for fabricating gamma- and X-ray detectors. Our investigations, reported here, are focused on producing high-quality (Cd,Mn)Te crystals with high resistivity (10{sup 9} {Omega}-cm) by the Bridgman method. As-grown, undoped (Cd,Mn)Te crystals are typically p-type, signifying that they contain excess Cd vacancies (acting as acceptors), accumulated during growth. Doping with vanadium atoms, which function as compensating centers, results in a semi-insulating material (Cd,Mn)Te:V. Properly annealing the platelets in cadmium vapors at uniform temperature reduces the number of cadmium vacancies, and lowers the level of the vanadium doping required for compensation. We found that annealing in cadmium vapors not only decreases the concentration of the native cadmium vacancies but also improves the crystal's quality. Infrared observations of the interior of the samples show that annealing in a temperature gradient perpendicular to the platelet has an additional effect, viz., the tellurium precipitates migrate towards the side where the temperature is higher. We demonstrate, with IR pictures of monocrystalline (Cd,Mn)Te:V platelets cut parallel to the (111) crystal planes, the influence on tellurium inclusions and precipitates of various conditions of annealing in cadmium vapors