The self-diffusion coefficient of U decreased from 3 x 10/sup -9/ cm/sup 2//sec at 785 deg C to 2.1 x 10/sup -11/ cm/sup 2//sec at 760 deg C. At temperatares high in the beta phase, the plots of log C vs. X/sup 2/ are curved, indicating that self-diffusion in beta U does not take place by isotropic volume diffusion alone. (auth
The diffusion coefficients of plutonium in uranium/plutonium mixed oxide single crystals at varying ...
The mechanism of dimensional instability of irradiated uranium is under investigation. In order to c...
Sorption and diffusion of uranium in sodium bentonite MX-80 were measured in aerobic conditions. The...
"July 1960""Partial Report - Metallurgy Division Program 4.1.2"Bibliography: p. 20.Operated by the U...
The self-diffusion coefficient or uranium was measured at four temperatures in the gamma phase. The ...
"July 1959""Portions of the material in this report have appeared in the following Metallurgy Divisi...
The diffusion coefficient of tracer amounts of Au/sup 198/ in gamma U is described by an Arrhenius-t...
Diffusion at infinite dilution of U in metals, with particular emphasis in those used in nuclear fac...
A "Kirkendall-effect" experiment with a very slight concentration gradient showed that diffusion tak...
The mechanism of dimensional instability of uramium is under investigation. Ih order to confirm an a...
Uranium self-di?usion coe cients were measured in UO2 single crystals through an original methodolog...
The diffusion process in uranium and its alloys was studied from 550 to 1075 deg C with diffusion co...
68 p.Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 1961.U of I OnlyRestricted to the U...
International audienceThis paper describes an original method to measure the plutonium self-diffusio...
ABS>A review of laboratory diffusion studies on uranium and its compounds and alloys is presented. I...
The diffusion coefficients of plutonium in uranium/plutonium mixed oxide single crystals at varying ...
The mechanism of dimensional instability of irradiated uranium is under investigation. In order to c...
Sorption and diffusion of uranium in sodium bentonite MX-80 were measured in aerobic conditions. The...
"July 1960""Partial Report - Metallurgy Division Program 4.1.2"Bibliography: p. 20.Operated by the U...
The self-diffusion coefficient or uranium was measured at four temperatures in the gamma phase. The ...
"July 1959""Portions of the material in this report have appeared in the following Metallurgy Divisi...
The diffusion coefficient of tracer amounts of Au/sup 198/ in gamma U is described by an Arrhenius-t...
Diffusion at infinite dilution of U in metals, with particular emphasis in those used in nuclear fac...
A "Kirkendall-effect" experiment with a very slight concentration gradient showed that diffusion tak...
The mechanism of dimensional instability of uramium is under investigation. Ih order to confirm an a...
Uranium self-di?usion coe cients were measured in UO2 single crystals through an original methodolog...
The diffusion process in uranium and its alloys was studied from 550 to 1075 deg C with diffusion co...
68 p.Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 1961.U of I OnlyRestricted to the U...
International audienceThis paper describes an original method to measure the plutonium self-diffusio...
ABS>A review of laboratory diffusion studies on uranium and its compounds and alloys is presented. I...
The diffusion coefficients of plutonium in uranium/plutonium mixed oxide single crystals at varying ...
The mechanism of dimensional instability of irradiated uranium is under investigation. In order to c...
Sorption and diffusion of uranium in sodium bentonite MX-80 were measured in aerobic conditions. The...
DOI
Add to ORKG