EFFECTIVENESS OF COPPER AND BRONZE FOR ZINC CAPTURE

A series of experiments was conducted to determine the efficacy of using copper and bronze sheet and screen under high vacuum conditions to capture zinc vapor. The experiments were conducted in a parametric manner using a fixed zinc vaporization temperature (350°C) but varying the filter temperature from ambient to 550°C. Consistent with previous work, metallic zinc was deposited at low temperatures, but the deposit was non‐adherent. At an intermediate temperature range (350‐450°C), the deposit formed an alloy with both copper and bronze materials. At higher temperatures (> 500°C) the zinc did not deposit on the surfaces likely due to its high vapor pressure. Additional testing to optimize the zinc 'getter' chemistry and surface condition is warranted