Add to ORKGAlloy X-750 is a nickel base alloy that is often used in nuclear power systems for it`s excellent corrosion resistance and mechanical properties. The present study examines the microstructure and composition profiles in a heat of Alloy X-750 before and after neutron irradiation
Radiation-induced changes in composition are studied because these changes can degrade failure of ma...
The microstructure and nanomechanical properties of three samples of the modified stainless steel (r...
The microstructure and nanomechanical properties of three samples of the modified stainless steel (r...
Microstructural and microchemical evolution of an Alloy X-750 heat under neutron irradiation was stu...
This paper presents the effects of neutron irradiation on the fracture behavior and deformation micr...
The in-service degradation of reactor core materials is related to underlying changes in the irradia...
Microstructure of Waspaloy and DT750 Ni-base superalloys was investigated after the heat treatment a...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
The corrosion resistance of Inconel X-750 alloy is strongly dependent on the microstructure. In this...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
The corrosion resistance of Inconel X-750 alloy is strongly dependent on the microstructure. In this...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
Radiation-induced changes in composition are studied because these changes can degrade failure of ma...
The microstructure and nanomechanical properties of three samples of the modified stainless steel (r...
The microstructure and nanomechanical properties of three samples of the modified stainless steel (r...
Microstructural and microchemical evolution of an Alloy X-750 heat under neutron irradiation was stu...
This paper presents the effects of neutron irradiation on the fracture behavior and deformation micr...
The in-service degradation of reactor core materials is related to underlying changes in the irradia...
Microstructure of Waspaloy and DT750 Ni-base superalloys was investigated after the heat treatment a...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
The corrosion resistance of Inconel X-750 alloy is strongly dependent on the microstructure. In this...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
The corrosion resistance of Inconel X-750 alloy is strongly dependent on the microstructure. In this...
International audienceThe issue of neutron irradiation embrittlement of Reactor Pressure Vessel stee...
Radiation-induced changes in composition are studied because these changes can degrade failure of ma...
The microstructure and nanomechanical properties of three samples of the modified stainless steel (r...
The microstructure and nanomechanical properties of three samples of the modified stainless steel (r...