Nature of the green luminescent center in zinc oxide

EPR, optical absorption, and photoluminescence spectroscopies are used to characterize a wide range of different ZnO phosphor powders. A good correlation is generally observed between the 510-nm green emission intensity and the density of paramagnetic isolated oxygen vacancies. Both quantities are found to peak at a free-carrier density of about 1.4x10{sup 18}cm{sup -3}. The green emission intensity can be strongly influenced by free-carrier depletion at the particle surface, especially for small particles and/or low doping. The data suggest that the green PL in ZnO phosphors is due to recombination of electrons in singly occupied oxygen vacancies with photoexcited holes in the valence band