Strength and flexibility of bulk high-{Tc} superconductors

Strength, fracture toughness, and elastic modulus data have been gathered for bulk high-temperature superconductors, commercial 99.9% Ag, and a 1.2 at.% Mg/Ag alloy. These data have been used to calculate fracture strains for bulk conductors. The calculations indicate that the superconducting cores of clad tapes should begin to fracture at strains below 0.2%. In addition, residual strains in Ag-clad (Bi,Pb){sub 2}Sr{sub 2}Ca{sub 2}Cu{sub 3}O{sub x} tapes have been measured by neutron diffraction. An explanation is offered for why many tapes appear to be able to tolerate large strains before exhibiting a reduction in current transport