Experimental investigations of material models for Ti-6A1-4V and 2024-T3

This report describes studies of the deformation and failure behavior of Ti-6Al-4V and 2024-T3 aluminum. Data was obtained at high strain rates and large strains using the split Hopkinson pressure bar technique. This information, plus additional data from the literature, was used to critically evaluate the ability of the Johnson Cook material model to represent the deformation and failure response of Ti-6AMV and 2024-T3 under conditions relevant to simulations of engine containment and the influence of uncontained engine debris on aircraft structures. This model is being used in the DYNA3D finite element code, which is being developed/validated for evaluating aircraft/engine designs relative to the federal airworthiness standards and for improving mitigation/containment technology. The results of the experimental work reported here were used to define a new set of material constants for the strength component of the Johnson Cook model for Ti-6Al-4V and 2024-T3. The capabilities and limitations of the model are reviewed. The model can accurately represent the stress-strain response of the materials. The major concern with the Johnson Cook material model is its ability to accurately represent the stress - strain rate response at strain rates greater than 10{sup 3}-10{sup 4} s{sup {minus}1}. Additional work is also needed to adequately account for failure via shear localization, which was the dominant failure mode at high strain rates in both materials. Failure modeling in both Ti-6Al-N and 2024-T3 will be considered further in future reports