Oxygen transport in the Sr{sub 2}Fe{sub 3{minus}x}Co{sub x}O{sub y} system.

The mixed-conducting Sr-Fe-Co oxide has potential use as a gas separation membrane. Its superior oxygen transport reveals the feasibility of using oxide membranes in large-scale oxygen separation. Sr{sub 2}Fe{sub 3{minus}x}Co{sub x}O{sub y} (with x = 0.0, 0.3, 0.6, and 1.0) samples were made by solid state reaction. To understand the oxygen transport mechanism in this system, conductivity and thermogravimetry experiments were conducted at high temperature in various oxygen partial pressure environments. The oxygen diffusion coefficient was determined from the time relaxation transient behavior of the specimen after switching the surrounding atmosphere. Mobility of the charge carrier was derived from relative conductivity and weight changes. X-ray diffraction experiments were carried out on these samples to determine their crystal structures