Ultrasonic characterization of silicate glasses, polymer composites and hydrogels

UnrestrictedIn many applications of material designing and engineering, high-frequency linear viscoelastic properties of materials are essential. Traditionally, the high-frequency properties are estimated through the time-temperature superposition (WLF equation) of low-frequency data, which are questionable because the existence of multi-phase in elastomer compounds. Moreover, no reliable data at high frequencies over MHz have been available thus far.; Ultrasound testing is cost-effective for measuring high-frequency properties. Although both ultrasonic longitudinal and shear properties are necessary in order to fully characterize high-frequency mechanical properties of materials, longitudinal properties will be extensively explored in this thesis. Ultrasonic pulse echo method measures longitudinal properties.; A precision ultrasonic measurement system has been developed in our laboratory, which allows us to monitor the in-situ bulk and/or surface properties of silicate glasses, polymer composites and even hydrogels. The system consists of a pulse-echo unit and an impedance measurement unit. A pulse echo unit is explored mainly.; First, a systematic procedure was developed to obtain precise water wavespeed value. A calibration curve of water wavespeed as a function of temperature has been established, and water wavespeed at 23 °C serves as a yardstick to tell whether or not a setup is properly aligned.; Second, a sound protocol in calculating attenuation coefficient and beam divergence effects was explored using three kinds of silicate glass of different thicknesses.; Then the system was applied to four composite slabs, two slabs for each type of fiberglass reinforced plastics, phenolic and polyester manufactured under different processing conditions: one was made by the normal procedures and the other with deliberate flaws such as voids, tapes and/or prepared at improper operation temperature and pressure. The experiment was conducted under the double blind test protocol. After carefully and methodically analyzing the data, we are able to detect defected specimens from all the specimens supplied to us, differentiate polyester-based composite from the phenolic-based composite and even recognized types of defects.; Lastly, ultrasonic monitoring of advancement of the swollen-unswollen fronts, and hence monitor phase transition from glassy state to rubbery state, of poly(acrylic-acid) hydrogel of one of the three different crosslinking densities is performed. With ultrasonic measurement, swelling monitoring is possible since the structural and mechanical changes during swelling of a dry hydrogel are related to changes in density and elastic constants. Using our carefully developed methodology from previous chapters, we may obtain and monitor average acoustic properties of each layer of hydrogel as it swells