Effect of load voltage on thin-film cuprous sulfide - cadmium sulfide solar cells thermally cycled in a simulated space environment /

Thin-film Cu2S-CdS solar cells, loaded at various fixed values of load resistance, were thermally cycled for 1429 cycles in a simulated space environment. Cell performance was measured under controlled conditions in air before and after thermal cycling. These data were used to determine the effect of load voltage on cell performance. The performance of the cells was relatively independent of load voltage up to about 0.39 volt. This appears to be a threshold voltage, beyond which there was a significant loss in cell performance. Fortunately, this threshold voltage appears to be sufficiently higher than the maximum power voltage of 0.33 volt so that it can be avoided in most applications.Prepared by Lewis Research Center.N72-13716.Includes bibliographical references (p. 10-11).Thin-film Cu2S-CdS solar cells, loaded at various fixed values of load resistance, were thermally cycled for 1429 cycles in a simulated space environment. Cell performance was measured under controlled conditions in air before and after thermal cycling. These data were used to determine the effect of load voltage on cell performance. The performance of the cells was relatively independent of load voltage up to about 0.39 volt. This appears to be a threshold voltage, beyond which there was a significant loss in cell performance. Fortunately, this threshold voltage appears to be sufficiently higher than the maximum power voltage of 0.33 volt so that it can be avoided in most applications.Mode of access: Internet