The Effect of Step-Like Martensitic Transformation on the Magnetic Entropy Change of Ni\u3csub\u3e40.6\u3c/sub\u3eCo\u3csub\u3e8.5\u3c/sub\u3eMn\u3csub\u3e40.9\u3c/sub\u3eSn\u3csub\u3e10\u3c/sub\u3e Unidirectional Crystal Growth with the Bridgman-Stockbarger Technique

We report a step-like martensitic transformation and its effect on magnetocaloric properties in Ni40.6Co8.5Mn40.9Sn10 unidirectional crystal grown using the Bridgman-Stockbarger technique followed by vacuum annealing at 1173 K for 72 h. This alloy undergoes successive first-order phase transitions which are attributed to the monotonic compositional variation along the crystal growth direction; the latter results in the increase of the full-width at half-maximum of the magnetic entropy change as a function of temperature (δTFWHM). For a magnetic field change of 2 and 5 T, the maximum magnetic entropy change are 9.7 and 16.0 J kg-1 K-1 with an extended δTFWHM of 11 and 23 K, respectively. The average hysteresis loss for a field change of 2 T is 19 J kg-1 reducing the refrigerant capacity by 17%